Bücher von Diogo Bevilaqua

The application of internal coating with plaster paste is an executive method widely used outside the country. With the constant technological variation and the need to reduce steps and execution time of activities, this coating has been gaining more and more space in the national scenario. Thus, this work aims to evaluate the use of this type of coating, analyzing its physical properties (tensile adhesion strength) when the thicknesses of the applied layers vary by 1.5, 2.0 and 2.5 cm. The results showed that the coating, especially in the thickness of 1.5 cm, did not meet the minimum resistance established by NBR 13749. Material and labor aspects were also surveyed in real situations of use through the application of questionnaires in eight companies. It was found that the use of internal coating with gypsum paste still needs greater adaptation by traders and a greater supply of qualified labor to be able to compete effectively with traditional mortar coatings.

La aplicación de revestimiento interno con pasta de yeso es un método ejecutivo ampliamente utilizado en el exterior. Con la constante variación tecnológica y la necesidad de reducir pasos y tiempo de ejecución de las actividades, este revestimiento viene ganando cada vez más espacio en el escenario nacional. Así, este trabajo tiene como objetivo evaluar el uso de este tipo de revestimiento, analizando sus propiedades físicas (resistencia a la tracción) cuando los espesores de las capas aplicadas varían en 1,5, 2,0 y 2,5 cm. Los resultados mostraron que el revestimiento, especialmente en el espesor de 1,5 cm, no cumplía la resistencia mínima establecida por la norma NBR 13749. También se estudiaron los aspectos materiales y laborales en situaciones reales de uso mediante la aplicación de cuestionarios en ocho empresas. Se constató que la utilización de revestimientos internos de cartón-yeso aún necesita una mayor adaptación por parte de los comerciantes y una mayor oferta de mano de obra cualificada para poder competir eficazmente con los revestimientos tradicionales de mortero.

L'application d'un revêtement interne avec de la pâte de plâtre est une méthode exécutive largement utilisée en dehors du pays. Avec l'évolution technologique constante et la nécessité de réduire les étapes et le temps d'exécution des activités, ce revêtement a gagné de plus en plus d'espace dans le scénario national. Ce travail vise donc à évaluer l'utilisation de ce type de revêtement, en analysant ses propriétés physiques (résistance à la traction) lorsque les épaisseurs des couches appliquées varient de 1,5, 2,0 et 2,5 cm. Les résultats ont montré que le revêtement, en particulier dans l'épaisseur de 1,5 cm, ne répondait pas à la résistance minimale établie par la norme NBR 13749. Les aspects liés aux matériaux et à la main-d'¿uvre ont également été étudiés dans des situations d'utilisation réelles, par le biais de questionnaires dans huit entreprises. Il a été constaté que l'utilisation de revêtements intérieurs en plaques de plâtre nécessite encore une plus grande adaptation de la part des commerçants et une plus grande offre de main-d'¿uvre qualifiée pour pouvoir concurrencer efficacement les revêtements traditionnels en mortier.

L'applicazione di un rivestimento interno con pasta di gesso è un metodo esecutivo ampiamente utilizzato anche all'estero. Con la costante variazione tecnologica e la necessità di ridurre i passaggi e i tempi di esecuzione delle attività, questo rivestimento ha conquistato sempre più spazio nel panorama nazionale. Il presente lavoro si propone quindi di valutare l'utilizzo di questo tipo di rivestimento, analizzandone le proprietà fisiche (resistenza a trazione) al variare degli spessori degli strati applicati di 1,5, 2,0 e 2,5 cm. I risultati hanno mostrato che il rivestimento, soprattutto nello spessore di 1,5 cm, non soddisfa la resistenza minima stabilita dalla norma NBR 13749. Anche gli aspetti relativi ai materiali e alla manodopera sono stati analizzati in situazioni reali di utilizzo attraverso l'applicazione di questionari in otto aziende. È emerso che l'uso del rivestimento interno in cartongesso necessita ancora di un maggiore adattamento da parte dei commercianti e di una maggiore disponibilità di manodopera qualificata per poter competere efficacemente con i tradizionali rivestimenti in malta.

Die Innenbeschichtung mit Gipspaste ist eine im Ausland weit verbreitete Ausführungsmethode. Mit der ständigen technologischen Veränderung und der Notwendigkeit, die Arbeitsschritte und die Ausführungszeit zu reduzieren, hat diese Beschichtung im nationalen Szenario immer mehr Raum eingenommen. Ziel dieser Arbeit ist es daher, die Verwendung dieser Art von Beschichtung zu bewerten und ihre physikalischen Eigenschaften (Zugfestigkeit) zu analysieren, wenn die Dicke der aufgetragenen Schichten um 1,5, 2,0 und 2,5 cm variiert. Die Ergebnisse zeigten, dass die Beschichtung, insbesondere in der Dicke von 1,5 cm, die in NBR 13749 festgelegte Mindestbeständigkeit nicht erreicht. Material- und Arbeitsaspekte wurden auch in realen Anwendungssituationen durch die Anwendung von Fragebögen in acht Unternehmen untersucht. Es wurde festgestellt, dass die Verwendung von Gipskarton-Innenverkleidungen noch einer stärkeren Anpassung durch die Gewerbetreibenden und eines größeren Angebots an qualifizierten Arbeitskräften bedarf, um wirksam mit den traditionellen Mörtelbeschichtungen konkurrieren zu können.