Bücher von Zehira Belamri

Kaolin is one of the most widely used mineral raw materials in ceramic compositions. The study described in this work concerns local kaolins used in the ceramics industry, i.e. kaolins from Djebel Debbagh and Tamazert. The elaboration and characterization of materials prepared from the two types of kaolins DD3P type 22% alumina, DD3R type 36% alumina and derivatives of another local kaolin KT2 were carried out by different analytical methods particularly : DRX, ATG, and SEM; we therefore deduce the mineralogical composition of these products. The thermal behavior of the two kaolins, heated between 1000°C and 11000°C and 1300°C and quenched, shows new phases: mullite from 1000°C and cristobalite nanocrystals from 1150°C. The dilatometric behavior of mixtures prepared from these kaolins in the raw state and sintered at 1200°C shows the various shrinkages significant of the transformations of the constituents of each mixture during heating. Temperature and holding time have an effect on the mechanical properties of the prepared materials.

O caulino é uma das matérias-primas minerais mais utilizadas nas composições cerâmicas. O estudo descrito neste trabalho diz respeito aos caulins locais utilizados na indústria cerâmica, ou seja, os caulins de Djebel Debbagh e Tamazert. A elaboração e a caraterização dos materiais preparados a partir dos dois tipos de caulins DD3P tipo 22% alumina, DD3R tipo 36% alumina e derivados de outro caulim local KT2 foram efectuadas por vários métodos de análise, nomeadamente: DRX, ATG e SEM; a composição mineralógica destes produtos é assim deduzida. O comportamento térmico dos dois caulins, aquecidos entre 1000°C e 11000°C e 1300°C e temperados, mostra novas fases: mulita a partir de 1000°C e nanocristais de cristobalita a partir de 1150°C. O comportamento dilatométrico das misturas preparadas a partir destes caulins no estado bruto e sinterizadas a 1200°C mostra as diferentes retracções significativas das transformações dos constituintes de cada mistura durante o aquecimento. A temperatura e o tempo de espera têm um efeito sobre as propriedades mecânicas dos materiais preparados.

El caolín es una de las materias primas minerales más utilizadas en las composiciones cerámicas. El estudio descrito en este trabajo se refiere a los caolines locales utilizados en la industria cerámica, es decir, los caolines de Djebel Debbagh y Tamazert. La elaboración y la caracterización de los materiales preparados a partir de los dos tipos de caolines DD3P tipo 22% de alúmina, DD3R tipo 36% de alúmina y derivados de otro caolín local KT2 se llevaron a cabo mediante varios métodos de análisis en particular: DRX, ATG y SEM; se deduce así la composición mineralógica de estos productos. El comportamiento térmico de los dos caolines calentados entre 1000°C y 11000°C y 1300°C y apagados, muestra nuevas fases; mullita a partir de 1000°C y nanocristales de cristobalita a partir de 1150°C. El comportamiento dilatométrico de las mezclas preparadas a partir de estos caolines en estado bruto y sinterizados a 1200°C muestra las diferentes contracciones significativas de las transformaciones de los constituyentes de cada mezcla durante el calentamiento. La temperatura y el tiempo de mantenimiento influyen en las propiedades mecánicas de los materiales preparados.

Il caolino è una delle materie prime minerali più utilizzate nelle composizioni ceramiche. Lo studio descritto in questo lavoro riguarda i caolini locali utilizzati nell'industria ceramica, ovvero i caolini di Djebel Debbagh e Tamazert. L'elaborazione e la caratterizzazione dei materiali preparati con i due tipi di caolino DD3P al 22% di allumina, DD3R al 36% di allumina e i derivati di un altro caolino locale, il KT2, sono state effettuate con diversi metodi di analisi, in particolare: DRX, ATG e SEM; è stata quindi dedotta la composizione mineralogica di questi prodotti. Il comportamento termico dei due caolini, riscaldati tra 1000°C e 11000°C e 1300°C e raffreddati, mostra nuove fasi: mullite a partire da 1000°C e nanocristalli di cristobalite a partire da 1150°C. Il comportamento dilatometrico delle miscele preparate con questi caolini allo stato grezzo e sinterizzati a 1200°C mostra i vari ritiri significativi delle trasformazioni dei costituenti di ciascuna miscela durante il riscaldamento. La temperatura e il tempo di mantenimento hanno un effetto sulle proprietà meccaniche dei materiali preparati.

Kaolin qwlqetsq odnim iz naibolee shiroko ispol'zuemyh mineral'nyh syr'ewyh materialow w keramicheskih kompoziciqh. Issledowanie, opisannoe w dannoj rabote, kasaetsq mestnyh kaolinow, ispol'zuemyh w keramicheskoj promyshlennosti, t.e. kaolinow Dzhebel' Debbag i Tamazert. Razrabotka i harakteristika materialow, prigotowlennyh iz dwuh tipow kaolinow DD3P tipa 22% glinozema, DD3R tipa 36% glinozema i proizwodnyh drugogo mestnogo kaolina KT2, prowodilas' razlichnymi metodami analiza, w chastnosti: DRX, ATG i SEM; takim obrazom, byl sdelan wywod o mineralogicheskom sostawe ätih produktow. Termicheskoe powedenie dwuh kaolinow, nagretyh ot 1000°C do 11000°C i 1300°C i zakalennyh, pokazywaet nowye fazy; mullit pri 1000°C i nanokristally kristobalita pri 1150°C. Dilatometricheskoe powedenie smesej, prigotowlennyh iz ätih kaolinow w syrom sostoqnii i spechennyh pri 1200°C, pokazywaet razlichnye usadki, znachitel'nye iz-za preobrazowanij komponentow kazhdoj smesi wo wremq nagrewa. Temperatura i wremq wyderzhki okazywaüt wliqnie na mehanicheskie swojstwa prigotowlennyh materialow.

Kaolin ist einer der am häufigsten verwendeten mineralischen Rohstoffe in keramischen Zusammensetzungen. Die in dieser Arbeit beschriebene Studie bezieht sich auf lokale Kaoline, die in der Keramikindustrie verwendet werden, nämlich die Kaoline von Jebel Debbagh und Tamazert. Die Entwicklung und Charakterisierung von Materialien, die aus den beiden Kaolinarten DD3P Typ 22% Aluminiumoxid, DD3R Typ 36% Aluminiumoxid und Derivaten eines anderen lokalen Kaolins KT2 hergestellt wurden, erfolgte durch verschiedene Analysemethoden, insbesondere : DRX, ATG und REM; daraus lässt sich die mineralogische Zusammensetzung dieser Produkte ableiten. Das thermische Verhalten der beiden Kaoline, die zwischen 1000°C und 11000°C sowie 1300°C erhitzt und abgeschreckt wurden, zeigt neue Phasen: Mullit ab 1000°C und Cristobalit-Nanokristalle ab 1150°C. Das dilatometrische Verhalten der Mischungen, die aus diesen Kaolinen im Rohzustand hergestellt und bei 1200°C gesintert wurden, zeigt die unterschiedlichen Schrumpfungen, die auf die Umwandlung der Bestandteile jeder Mischung während des Erhitzens hindeuten. Die Temperatur und die Haltezeit wirken sich auf die mechanischen Eigenschaften der hergestellten Materialien aus.

Le kaolin est l¿une des matières premières minérales les plus utilisées dans les compositions céramiques. L¿étude décrite dans ce travail concerne des kaolins locaux utilisés dans l¿industrie céramique ce sont les kaolins de Djebel Debbagh et de Tamazert. L'élaboration et la caractérisation des matériaux préparés à partir des deux types de kaolins DD3P type 22% alumine, DD3R type 36% alumine et des dérivés d¿autre kaolin local KT2 ont été effectuée par différentes méthodes d¿analyses particulièrement : DRX, ATG, et le MEB; on déduit donc la composition minéralogique de ces produits. Le comportement thermique des deux kaolins chauffées entre 1000°C et 11000°C et 1300°C et trempé, montre nouvelles phases; la mullite à partir de 1000°C et des nanocristaux de cristobalite à partir de 1150°C. Le comportement dilatométrique des mélanges préparés à base de ces kaolins à l¿état cru et frittés à 1200°C donne les différents retraits significatif des transformations des constituants de chaque mélange au cours de chauffage. La température et le temps de maintien ont un effet sur les propriétés mécaniques des matériaux préparés.